Building Materials Used in Construction

Building Materials Used in ConstructionIn the world of construction, the king of mental synthesis materials is cover. It is the most common material and it constitutes the base of a lot of constructions like structures, roads, bridges, tunnels, water pipes dams etc. It is an absolutely indispensable tool of civil engineers that is holdd for more than a century. Before its existence the largest portion of constructions was covered by two other materials, wood and stone, while the last years is very widespread the apply of the reinforced concrete which is concrete with bars of steel in it.Concrete AnalysisWe send away say that concrete is a type of an artificial stone, a mixture of four elements cementum, water, sand and meats that is succeed by the process of hydration. This process converts the slushiness mixture into an artificial stone just in a few hours. The mischievous concrete continue to harden for many years but in the s all the same fist days has already taken more than 70% of its occur resistance and in 28 days pull up stakes have take practically its total resistance. Making the concrete we should be very cargonful to the proportioning. cement and water are the two chemically reactive elements while sand and aggregates are chemically inactive. The proportions of each material in the mixture affect the properties of the final hardened concrete. As the cement (created by crushing up clay and limestone to take aimher and roasting it in a kiln) content increases, so does the strength and military posture of the concrete (a good rate is 12%), the water should be pure and not overtop the 17% because the mixture will be weak and as it concerns the aggregates, too much fine aggregate gives a sticky mix while too much coarse aggregate gives a harsh mix. any these materials together give to concrete some properties and the basic property is that concrete has a very high resistance in compression but start resistance in tension. For this ration ality, as it mentioned before, we use a lot the reinforced concrete because the steel bars can handle the concrete in tension. As exists the term of resistance so on the opposite will be another term, this of fatigue.Explanation of FatigueFatigue is a process of progressive, permanent geomorphologic change occurring in a material which is subjected to conditions that produce time fluctuating stresses and strains. The structural changes appeal in cracks or complete fracture afterward a sufficient number of fluctuations. The fatigue process occurring in concrete has been under investigation since about 1900 with the majority of the significant work having been done during the past cardinal years. This process has been observed in concrete under repeated compressive and flexural freight and small amounts of experimental work show that it likewise occurs under reversed flexural loading and repeated tensile loading.Reasons of damage on concreteIn perfect conditions, that means an art ificial environment of a laboratory and without considering the human mistake, concrete can last without any corrosion about 50 years. But in our environment the fatigue of concrete will start to appear in 30 years and after that the construction need to be watched and maintained. We can examine the fatigue of concrete with two different points of view macro scale and little scale.As it concerns the fatigue of the concrete from a macro scale view we can refer the following apprehensions. Concrete is a mixture of materials that is decayed in time so the first reason of the fatigue of the concrete is because of its old. Another cause is the animated alkaline environment of the atmosphere and this phenomenon is appeared especially at the urban centers because of the exhausts that are coming out from vehicles and factories. The proximity of the concrete in the water environment, such as big amounts of salt in the air and big amounts of moisture, is also an erosive factor. Furthermore , the boisterous change of the temperature as much as in winter and summer months in combination with the high amounts of moisture cause intense shrinkages and expansions on concrete. It is characteristically observed that the boisterous change of temperature per 10 C doubles the velocity of corrosion in concrete. Earthquake is the most dangerous reason of all. It can affect the concrete less or too much. It can cause a damage that is invisible but this may affect the building for years creating a bigger damage later. But the earthquake also can cause a complete fracture of concrete. The last important reason tin the macro scale view is the fire. During the fire the most common problems that are presenting are firstly the fracture part of the concrete because of the violent victimization of pressures from the evaporation of the water contain in concrete, secondly the thermal expansion of the concrete which also leads to fracture and finally the various change of stresses on concret e because of the abrupt frost extinguishing of fire.If we want to study it from a micro scale view we could refer the following causes of the fatigue on concrete sulphate Deterioration. Sodium, magnesium, and calcium sulfates are salts These sulfates react chemically with the hydrated lime and hydrated aluminate in cement paste and form calcium sulfate and calcium sulfoaluminate. The book of account of these reaction byproducts is greater than the volume of the cement paste from which they are formed, causing disruption of the concrete from expansion.Alkali Aggregate Reaction. Certain types of sand and aggregate, such as opal, chert, and flint, or volcanics with high silica content, are reactive with the calcium, sodium, and potassium hydroxide alkalies in portland cement concrete. These reactions, though observed and studied for more than 50 years, persevere poorly defined and little understood. Some concrete containing alkali reactive aggregate shows immediate evidence of dest ructive expansion and descent. Other concrete superpower remain undisturbed for many years. Petrographic examination of reactive concrete shows that a gel is formed around the reactive aggregate. This gel undergoes extensive expansion in the presence of water or water vapor (a relative humidity of 80 to 85 percent is all the water required), creating tension cracks around the aggregate and expansion of the concrete. If unconfined, the expansion within the concrete is first apparent by pattern cracking on the surface.Deterioration Cause by Cyclic Freezing and Thawing. Freeze-thaw deterioration is a common cause of damage to concrete constructed in the colder climates. For freeze-thaw damage to occur, the following conditions must existThe concrete must undergo cyclic freezing and thawing.b. The pores in the concrete, during freezing, must be nearly saturated with water (more than 90 percent of saturation).Water experiences about 15 percent volumetric expansion during freezing. If t he pores and capillaries in concrete are nearly saturated during freezing, the expansion exerts tensile forces that fracture the cement mortar matrix. This deterioration occurs from the outer surfaces inward in almost a layering manner. The rate of progression of freeze-thaw deterioration depends on the number of cycles of freezing and thawing, the degree of saturation during freezing, the porosity of the concrete, and the vulnerability conditions.Acid Exposure. The more common sources of acidic exposure involving concrete structures occur in the vicinity of under-ground mines. Drainage waters exiting from such mines can contain acids of sometimes unexpectedly low pH value. A pH value of 7 is defined as neutral. Values higher than 7 are defined as basic, while pH values lower than 7 are acidic. A 15- to 20-percent solution of sulfuric acid will have a pH value of about 1. Such a solution will damage concrete very rapidly. Acidic waters having pH values of 5 to 6 will also damage co ncrete, but only after long exposure.Construction Defects. Some of the more common types of damage to concrete caused by construction defects are rock pockets and honeycombing, form failures, dimensional errors, and finishing defects. fret and rock pockets are areas of concrete where voids are left due to failure of the cement mortar to fill the spaces around and among coarse aggregate particles.SolutionsGenerally when a crack affects the performance of the structure, then we will reanimate it to restore its structural properties. Epoxy injection is typically the basis for this type of repair, with or without added reinforcement. The injected epoxy is really stronger than the concrete and can restore the concrete strength. To use epoxy injection to repair a crack, the crack is first cleaned by vacuuming or flushing with water to get out any dirt or contamination. The cracks on the surface are then sealed with an epoxy gel to prevent the injected epoxy from running out. pellet an d venting ports are installed and the epoxy is injected. High pressure is not used since that could actually widen the cracks. Once the cracks have been filled, the ports and surface seals are removed, typically by grinding the surfaces flush with the concrete matrix. When concrete is too deteriorated for epoxy injection, then all unsound concrete is removed and new concrete is placed. (http//www.concretenetwork.com/concrete-repair/structure.html) (accessed 17/04/2011)Portland cement mortar may be used for repairing defects on surfaces not prominently exposed, where the defects are too wide for dry tamp down filling or where the defects are too shallow for concrete filling and no deeper than the far side of the reinforcement that is nearest the surface. Repairs may be made either by use of shotcrete or by hand application methods. Replacement mortar can be used to make shallow, small size repairs to new or discolour concrete.Surface grinding can be used to repair some bulges, offs ets, and other irregularities that exceed the desired surface tolerances. Excessive surface grinding, however, may run in weakening of the concrete surface, exposure of easily removed aggregate particles, or unsightly appearance.The dry pack concrete repair technique shall be limited to areas that are small in width and relatively deep, such as core holes, holes left by the removal of form ties, cone-bolt and she-bolt holes, and narrow slots wind for repair of cracks. Epoxy bonded dry pack shall be used for critical repairs or for repairs expected to be exposed to severe service conditions. Dry pack mortar shall consist of type I or II Portland cement, clean sand that will pass a 1.18-mm sieve, and clean water.Epoxy-bonded concrete is defined as freshly mixed Portland cement concrete that is placed over a fluid epoxy resin bond coat on hardened breathing concrete. Epoxy-bonded concrete repair may be used when the depth of repair is 30 cm 50 cm or greater.Resin injection is used to repair concrete that is cracked or delaminated and to seal cracks in concrete to water leakage. Two basic types of resin and injection techniques are used to repair Reclamation concrete. Epoxy Resins and Polyurethane Resins.ConclusionWithout concrete, the history of constructions would not be the same and our concern must be to make it stronger and friendlier to the environment and make even more impressive constructions.